Influence of Silica Nanoparticles on the Thermal Transitions and Structure of PHBA-PET Nanocomposites

F. Miranda, A. Acevedo
University of Puerto Rico, PR

Keywords: nanocomposites, liquid crystals, silica

Abstract:

Composite films were produced by direct melt-blending of the polymer with up to 1.5 vol% loadings in a Thermo-Haake MiniLab2 twin-screw extruder. Thermal transitions were determined by differential scanning calorimetry and thermogravimetric analysis. Structure and morphology were analyzed by a combination of polarized optical microscopy, small-angle x-ray scattering (SAXS), and scanning electron microscopy. No significant changes were observed on the glass transition temperature, nevertheless the melting point showed a small tendency toward higher values at higher loadings. The nematic range decreased upon addition of particles, but was mostly unaffected by concentration. The maximum rate of degradation was displaced up to 30 ÂșC. A detrimental effect on the internal ordering of the polymer was also observed, as suggested by the reduction and eventual disappearance of the characteristic SAXS peak. Micrographs show a smooth film surface and straight fracture planes (i.e. no fibrils). Silica particles improved the thermal properties of the polymer, yet as the loading increase results suggest a reduction of the nematic range and order.
 
 
Sessions Monday Tuesday Wednesday Thursday Authors Keywords Affiliations Search

TechConnect World 2011 Nanotech 2011 Clean Technology 2011 Microtech 2011 BioNanotech 2011 TechConnect Summit 2011
2011 Events | Program | Speaker | Short Courses Sponsor Exhibit/Showcase Press Venue Register
Subscribe | Contact | Site Map
© Copyright 2010 TechConnect World. All Rights Reserved.