Nano-structured Ni.15Cu.25 Zn.6Fe1.96 Ferrite

H. Zhang, R. Karmacharya, R. Tomcavage, D. Schofield, D. Xiao
Inframat Corporation, US

Keywords: nano-structured NiCuZn ferrite, low temperature co-fired ceramic, sol-gel, permeability

Abstract:

In this work, we use sol-gel process to synthesize the nano-structured Ni.15Cu.25Zn.6Fe1.96O4 ferrite. The formed nano-powder was pressed into toroid rings and sintered at 930C at air atmosphere. In order to comparison to the ferrite with the same formula fabricated by conventional solid-state reaction ceramic method, the sintered density of nano-structured Ni.15Cu.25Zn.6Fe1.96O4 is 5.25g/cm3, which is 5% higher than micro-structured Cu.25Zn.6Fe1.96O4, 5.0g/cm3. The magnetic characterization indicates that the Curie temperature is 115 oC for both ferrites. However, the initial permeability of nano-structured Ni.15Cu.25Zn.6Fe1.96O4 is over 444, but 205 for the micro-structured Ni.15Cu.25Zn.6Fe1.96O4. The permeability of the nano-structured ferrite is as double as that of the micro-structured ferrite.
 
 
Sessions Monday Tuesday Wednesday Thursday Authors Keywords Affiliations Search

TechConnect World 2011 Nanotech 2011 Clean Technology 2011 Microtech 2011 BioNanotech 2011 TechConnect Summit 2011
2011 Events | Program | Speaker | Short Courses Sponsor Exhibit/Showcase Press Venue Register
Subscribe | Contact | Site Map
© Copyright 2010 TechConnect World. All Rights Reserved.